    Structural, morphological, and magnetic characterizations of (Fe0.25Mn0.75)2O3 nanocrystals: A comprehensive stoichiometric determination
    (Elsevier Ltd, 2024-12-01)
    This report aims to investigate in depth FeMnO3, a material of interest due to its fascinating magnetic and multiferroic properties and its many applications in fields including lithium-ion batteries, microwave devices, and catalysis. However, understanding the precise stoichiometry of the material is crucial for a better comprehension of its physical properties. A cheap, simple, and repeatable sol-gel process was used to fabricate the FeMnO3 nanocrystals. Comprehensive multi-technique characterization of the as-fabricated FeMnO3 indicates that the main phase (94 wt%) is Fe0.5Mn1.5O3, although hematite appears as the minority phase (6 wt%). Magnetic characterization shows core-shell spin-glass like behavior, as well as paramagnetic-ferrimagnetic transitions and a Griffiths phase regime. EPR measurements revealed a strong and broad resonance line across the temperature range of 4.3 K–300 K, primarily influenced by the majority phase. The g-value decreases monotonically from 2.93 at 50 K to 2.18 at 300 K. There is a notable change in the resonance field and linewidth between 40 and 50 K, attributed to surface spin glass behavior. The EPR data below 50 K are in line with the core-shell model of (Fe0.25Mn0.75)2O3 nanoparticles. Below 50 K, the shell's spin system undergoes a transition from paramagnetic to spin-glass-like, with a critical temperature around 43 K. Above 50 K, the superparamagnetic minority phase significantly affects the temperature dependence of the resonance linewidth. These results hold particular importance as they advance our understanding of the intricate magnetic interactions present in FeMnO3. For the best possible use of this material platform in new technologies, such insights are essential.
  • Loading...
    Thumbnail Image
    Some of the metrics are blocked by your 
    consent settings
    Item type:Publication,
    Tailoring the Properties of Magnetite/PLA Nanocomposites: A Composition-Dependent Study
    (Multidisciplinary Digital Publishing Institute (MDPI), 2025)
    This study focused on composites of magnetite magnetic nanoparticles (MNP) and poly(lactic acid) (PLA) prepared via sonochemical synthesis. The evaluation of MNP loadings (2, 5, 10, 15, and 20 wt.%) provided insights into the structural and reactivity properties of the materials. Methods used included XRD, FT-IR and Raman spectroscopy, SEM and TEM microscopy, textural and thermal analysis (TG and DTA), and magnetic property measurements. The agreement between theoretical and experimental MNP loadings was good. XRD patterns showed predominantly MNP and semicrystalline phases, with a minor maghemite phase detected by FT-Raman and magnetic measurements. FT-IR analysis revealed interactions between MNP and PLA, confirmed by thermal analysis showing higher transition temperatures for the composites (145 °C) compared to pure PLA (139 °C). FT-Raman spectra also indicated that PLA helps prevent iron oxide oxidation, enhancing nanoparticle stability. SEM and TEM micrographs showed well-dispersed, spherical nanoparticles with minimal agglomeration, dependent on MNP loading. The nanocomposites exhibited low N₂ adsorption, resulting in low surface area (~2.1 m²/g) and porosity (~0.03 cm³/g). Magnetic analysis indicated that in the 2MNP/PLA sample, MNP were in a superparamagnetic-like regime at 300 K, suggesting good dispersion of 2 wt.% MNP in the PLA matrix.
      1